鋰電池漿料的*化混合脫泡方法

關鍵詞：鋰電池 漿料 混合 脫泡 公自轉 氣泡去除

Abstract:  The paste of litmus battery needs to be finely mixed before coating. But the tiny bubbles in the paste will have to negative affect for the coating procedure. A nonuniform coating flat of the litmus battery always cause badly defeats of products. This article focuses on the best solution for removing the bubbles in the litmus battery. Basically, the method of processing is the planetary paste mixer. But the key for removing bubbles is the setting mode of the mixer. By adjusting the speed of the revolution and the rotation freely, the effect of bubble removing could be controlled by the mixer. But the traditional paste mixer can only just change the ratio of planetary system. It couldn’t be fitted for the different pastes.

鋰電池是目前新能源領域中上升勢頭zui為迅猛的方向之一。特別是近兩年隨著中國國內政策調整及潔凈能源需求擴大，國內鋰電行業產能不斷增長，各鋰電供貨商都紛紛擴大生產能力，以求順應市場需求缺口擴大的趨勢。

其中，行星式真空混料脫泡機在鋰電池漿料混合的制程工藝中有著極大的應用推廣前景；主要原因有兩點。首先，經過有效去除亞微米級氣泡后的漿料的涂布效果有顯著提高。其二，此類經過脫泡處理的漿料可以有效提升極片的品質從而改善后端模組的良率。這是由已經廣泛應用此設備進行漿料處理的韓國三星、LG工廠的實際經驗得到的反饋。

行星式真空混料脫泡機主要工作原理是藉由設備的公轉及自轉產生合成運動，使漿料本身在料罐中不斷有序翻轉，從而將極細微氣泡擠出后由真空去除的過程（參見下圖中的運動合成模擬）。由于此設備只是利用物理本身重力的作用，沒有直接接觸的機械機構，所以可將物料中的亞微米級別氣泡全部排出。

以石墨負極材料的混合為例，由于石墨本身物理性質為高吸附性，所以漿料中的氣泡是難以通過自然靜置的方式排出的。而采用帶有攪拌機構的設備來進行氣泡混合的話則容易產生更多的氣泡。

我們采用TRILOS公司的PM1KV行星式真空混料脫泡機進行混合時，只需將石墨粉末與有機溶劑同時置于料罐之中（如上圖）。然后直接將料罐放入設備中即可進行混合脫泡作業。

   為了有效區分真空功能在漿料混合脫泡中的作用，可進行以下兩組不同的參數設置：

zui終的混合效果分別如下,

采用參數a即沒有使用真空功能的混合效果：

注意紅色部分標記出的為沒有被帶走的氣泡，依然在漿料表面附著，但顯然所有微氣泡都被排擠成為一個較大氣泡。

采用參數b即使用真空的功能的混合效果：

上圖中的單個大氣泡已經通過真空系統*去除，漿料混合均勻。

由此可見，即使是吸附能力*的石墨粉為主體的鋰電池漿料，在經過強力非接觸的混合及脫泡處理后，內部所有的氣泡都已經被排出。這對于接下來的涂布制程來說，可以有效的提高鋰電池漿料涂布質量，從而從源頭上改善產品由于涂布不均而造成的后端模組異常及不良。zui為關鍵的是，目前此方案是去除鋰電池漿料中亞微米級別氣泡的*解決辦法。同樣的，根據實際反饋案例來看；此設備對于三元材料、膠粘劑等相關漿料的混合脫泡也有著良好的實踐效果。